Soldering to Chassis

Does anyone have any advice on how to remove soldered leads directly to the chassis? The solder barely melts and I can't seem to remove it. I've also tried sanding the joint to expose unoxidized solder with no prevail. I had cranked my iron up to 800F and still no luck either

Also, any advice what to use to solder back to chassis as well?
__________________
"If it isn't broke, you aren't trying hard enough"
Reply With Quote
  #2  
Old 07-07-2018, 06:17 PM
WISCOJIM WISCOJIM is offline
VideoKarma Member
 
Join Date: Sep 2005
Location: Grand Chute, Wisconsin
Posts: 1,930
Using flux helps greatly. You need a large mass of heat to solder to a chassis, a small tipped 800 degree iron will have all the heat sucked out of it before it'll melt solder on a big chassis. There's nothing like a good old-fashioned American Beauty for chassis soldering. They can easily be found on ebay or at ham radio swap meets.



.
Reply With Quote
  #3  
Old 07-07-2018, 09:05 PM
bgadow's Avatar
bgadow bgadow is offline
VideoKarma Member
 
Join Date: Oct 2003
Location: Federalsburg, MD
Posts: 5,538
I second that, brute force wins. I have one that looks like the picture (different brand) plus a modern Weller that's a monster. Once used the latter to solder a hole in the radiator tank of an old Chevy and it was still perfect after nearly 20 years. In the dark the tip glows red. Don't do as my Dad did and touch it to see if it's hot enough
__________________
Bryan
Reply With Quote
  #4  
Old 07-07-2018, 10:44 PM
Electronic M's Avatar
Electronic M Electronic M is offline
M is for Memory
 
Join Date: Jan 2011
Location: Pewaukee/Delafield Wi
Posts: 9,788
Third that.

You need at least a 75W Iron to solder a chassis ground properly like the original work. I've got an older weller (must have been made in the last 30 years since it's orange), and a couple of 150W antique irons that eat chassis ground work for breakfast...They even make new grounds like it is nothing.

Something like a 45W or under iron is close to or below the thermal power rating of the chassis heatsink (and a chassis can be used as a heatsink).
__________________
Tom C.

What I want. --> http://www.videokarma.org/showpost.p...62&postcount=4

Reading between the scan lines since the mid 2000's.
Reply With Quote
Reply


Thread Tools
Display Modes

Posting Rules
You may not post new threads
You may not post replies
You may not post attachments
You may not edit your posts

BB code is On
Smilies are On
[IMG] code is On
HTML code is Off

Forum Jump


All times are GMT -5. The time now is 01:16 PM.



Powered by vBulletin® Version 3.8.4
Copyright ©2000 - 2018, Jelsoft Enterprises Ltd.
ęCopyright 2012 VideoKarma.org, All rights reserved.